Products

Removable type double coated tapes

Excellent reworkability without tearing.


Comparison

Please select the product name :



image

Product name

 G9000R/G9000RW

Suitable use

 For general-purpose and recycling purpose

Application
  • Computers/
  • AV

Features
  • No solvent used at coating process. UV curable manufacturing method.
  • High heat resistance ; can be used in environments of up to 100°C.
  • High adhesive quality (heat resistance and weather resistance) for wide ranging applications.
  • High processability for seal cutting (half cutting).
  • Removable model: Little paste left after an extended period of use.
Green tape

Structure

Structure

Specifications

Product name G9000R G9000RW*2
Main component Acrylic base Acrylic base
Carrier Nonwoven fabric Nonwoven fabric
Color Translucent Translucent
Adhesive thickness(µm) About 150 About 150
Release paper thickness(µm) About 150 About 150+120
Bonding strength
(N/20mm) *1		 15 15
St'd size (width & length) 500mm x 50m 500mm x 50m
Warranty period from manufacturing date 12 months 12 months

UL certificated. UL file No:( UL969 No.MH15431)
*1 180° peeling strength
*2 G9000RW: With both side release paper.


Application Example

Application Example
Suitable for adhesion of metal, plastic and urethane parts of household electrical appliances and office automation equipment, and of sites that require removal.

Top of page

Technical Data

1.Bonding strength on various type of substrate (180° peeling)


Test Piece condition
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Measuring condition: 23°C±5°C 60%±20%RH
Peeling speed: 300mm/min
Backing material: 25µm PET
  • [Left at RT for one hour before measurement]
Results
(N/20mm)
180° peeling strength Product name Substrate
SUS ABS Glass
G9000R 15.1 14.4 13.2

2.Holding power at different temperatures


Test Piece condition
Substrate: Stainless steel plate (SUS304)
Tape bonding area: 25mm x 25mm
Bonding condition: One stroke with 2-kg roller
  • [Left at RT for one hour and then at each temperature for 30 minutes before measurement]
  • [Creep length after one hour application of 1-kg load]
Results
Creep length(mm) Product name Measurement temperature
40°C 60°C 80°C 100°C
G9000R 0.2 0.2 0.3 0.4

3. Removable evaluation under each temperature by elapsed time (180° peeling)


Test Piece condition
Substrate: ABS plate
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Measuring condition: 23°C±5°C 60%±20%RH
Peeling speed: 300mm/min
Backing material: 25µm PET
  • [Left at RT for one hour and aged at a predetermined temperature for 8 weeks before measurement]
Results
(N/20mm)
Removable evaluation
(180° peeling strength)		 Product name Aging condition Measurement time
Initial 1week 2weeks 4weeks 8weeks
G4000 -30°C 14.4 19.3 18.6 19.0 17.5
60°C 14.4 20.4 19.8 21.2 22.9
40°C 90%RH 14.4 17.5 19.0 20.2 20.7
* Good. (There is no paste remainder to the substrate.)
Results
Top of page
coution
Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.