General-purpose double coated tapes
For applications that need to be dimensionally stable and thin.
- G9050/G9050W
- G9051
- G9052/G9052W
- S9951W-30

| G9052/G9052W | |
| For fixing thin parts | |
|
|
|

| Product name | G9052 | G9052W *2 |
|---|---|---|
| Main component | Acrylic base | Acrylic base |
| Carrier | About 25µm PET | About 25µm PET |
| Color | Transparent | Transparent |
| Adhesive thickness(µm) | About 85 | About 85 |
| Release paper thickness(µm) | Paper About 150 | Paper About 115 +120 |
| Bonding strength(N/20mm) | 15 | 15 |
| St'd size(width & length) | 500mm x 50m | 500mm x 50m |
| Warranty period from manufacturing date | 12 months | 12 months |
UL certificated. UL file No: (UL969 MH15431)
*1 180° peeling strength
*2 G9052W : With both side release paper

For mobile equipment, parts in LCD modules and cushioning materials such as urethane.
| Tape width: | 20mm |
|---|---|
| Bonding condition: | One stroke with 2-kg roller |
| Measuring condition: | 23°C±5°C 60%±20%RH |
| Peeling speed: | 300mm/min |
| Backing material: | 25µm PET |
- [Left at RT for one hour before measurement]
(N/20mm)
| 180° peeling strength | Product name | Substrate | |
|---|---|---|---|
| SUS | ABS | ||
| G9052 | 15.3 | 7.2 | |
| Substrate: | Stainless steel plate (SUS304) |
|---|---|
| Bonding area: | 25mm x 25mm |
| Bonding condition: | One stroke with 2-kg roller |
| Backing material: | 25µm PET |
- [Left at RT for one hour and then at each temperature for 30 minutes before measurement]
- [Creep length after one hour application of 1-kg load]
| Creep length(mm) | Product name | Measurement temperature | |
|---|---|---|---|
| 40°C | 80°C | ||
| G9052 | 0.2 | 0.2 | |
Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.