Impact force resistant type double coated tapes

Double coated tape series produced employing non-solvent manufacturing method suitable for fixing of structural components that need impact force resistance.


Comparison

Please select the product name :


image

Product Name

 G9400

Suitable use

 For impact force resistance, and fixing of acrylic windows or other parts.

Application
  • Cellular phones

Features
  • Environmentally friendly non-solvent manufacturing method.
  • Thin type with high impact force resistance and initial adhesion.
  • High adhesion to UV coated surface.
non-solvent manufacturing method

Structure

Structure

Specifications

Product Name G9400
Main component Acrylic base
Carrier Nonwoven fabric
Color Semi transparent
Adhesive thickness(µm) About 100
Release paper thickness(µm) About 135
Bonding strength(N/20mm) 8
St'd size(width & length) 500mm x 50m

* UL certificated. UL file NO.MH15431


Application Example

For fixing of window frames of mobile phone LCD displays and nameplates.

Top of page

Technical Data

1.Bonding strength on various type of substrate (180° peeling)


Test Piece condition
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Measuring condition: 23°C±5°C 60%±20%RH
Peel speed: 300mm/min
Backing material: 25µm PET
  • [Left at RT for one hour before measurement]
Results
(N/20mm)
Substrate SUS ABS Acrylic base
Peeling strength 8.0 8.6 8.8

2.Holding Power at different temperatures


Test Piece condition
Substrate: Stainless steel plate (SUS304)
Bonding area: 25mm x 25mm
Bonding condition: One stroke with 2-kg roller
  • [Left at RT for one hour and then at each temperature for 30 minutes before measurement]
  • [Creep length after one-hour application of 1-kg load]
Results
Measurement temperature 40°C 60°C 80°C
Creep length(mm) 0.2 1.8 2.9

3.Ball tack test (J. Dow method)


Results

Ball No:23 to 26

4.Impact force resistance


Test Piece condition
Substrate: ABS (50 mm square)/ Acrylic plate (15 mm square)
Bonding area: 15mm x 15mm
Test atmosphere: 10°C
Impact force: Dropping 300g weight onto the ABS face from a height of 15 cm.
  • [Left at RT for one day after adhesion, and then under each test condition for 30 minutes before measurement]
  • [Check whether the acrylic plate has been dropped]
Results

Impact force resistance(n=5):No dropped nor peeled portion found

Top of page
coution
Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.