Nitrile rubber base hotmelt adhesive tapes(non-carrier type)

For applications where strong adhesiveness is required, such as mutual adhesion of metal materials, and adhesion of a metal material and a plastic material.


Please select the product name :



image

Product name

 NP101G

Suitable use

 Adhesion of Aluminum name plates, and metal and plastic materials

Application
  • Computers/
  • AV/
  • Cellular phones/
  • Automobile

Features
  • Nitrile rubber base. High petroleum resistance.
  • Corresponding to the thermal activation method and solvent activation method (MEK).

Structure

Structure

Specifications

Product name NP101G
Main component NBR base
Carrier Non-carrier
Color Green
Adhesive thickness(µm) About 50
Release paper thickness(µm) About 60
Bonding strength(N/20mm) 13
St'd size(width & length) 400mm x 100m
Standard bonding condition Temperature: 130 to 160°C, Time: 5 to 15 sec, Pressure: 20 to 30 N/cm2

Application Example

For adhesion of Aluminum name plates, and metal and plastic materials.
* Unsuitable for adhesion of styrol materials.

Top of page

Technical Data

1.Bonding strength under different temperatures (Cleavage strength)


Test Piece condition
Substrate: 500 µm Aluminum / 5mm ABS
Bonding area: 40mm x 40mm
Bonding condition: Temperature: 140 °C, Pressure: 30 N/cm², Time: 45 sec.
Peeling speed 50mm/min.
  • [Left at each test temperature for 30 minutes before measurement]
Results
Results

2.Bonding strength at different temperatures (180° peeling)


Test Piece condition
Substrate: 50µm Aluminum / 300 µm Aluminum
Tape width : 20mm
Bonding condition: Temperature: 140 °C, Pressure: 30 N/cm², Time: 10 sec.
Peeling speed 100mm/min.
  • [Left at each test temperature for 30 minutes before measurement]
Results
Results

3.Reliability of bonding strength after adhesion under different conditions (180° peeling)


Test Piece condition
Substrate: 50µm Aluminum / 300 µm Aluminum
Tape width : 20mm
Bonding condition: Temperature: 140 °C, Pressure: 30 N/cm², Time: 10 sec.
Peeling speed 100mm/min.
  • [Left at each test temperature for 30 minutes before measurement]
Results
Results
Top of page
coution
Note on the characteristic data given - Data on the characteristics of the products described in this page based on the results of evaluations carried out by the company. This does not guarantee that the characteristics of the product conform with your usage environment. Before use, review the usage conditions based on evaluation data obtained from the equipment and substrates actually used.