Black colored type double coated tapes
Black, general-purpose double coated tapes suitable for adhesion of black parts.
Products Category Double coated tapes
Please select the product name :  
T3500SB

Product name

 T3500SB/T3500SBW

Suitable use

 General-purpose.

Application

 Computers / AV / Cellular phones / Automobiles

Features
  • High adhesive quality (heat resistance and weather resistance) for wide ranging applications.
  • Good holding power even at high temperature.
  • High processability for seal cutting (half cutting).
 
   
     

Structure

Specifications
Product name T3500SB T3500SB(※2)
Main component Acrylic base Acrylic base
Carrier Nonwoven fabric Nonwoven fabric
Color Black Black
Adhesive thickness(µm) About 150 About 150
Release paper thickness(µm) About 150 About 150+120
Bonding strength(N/20mm) 10 10
St'd size (width & length) 500mm x 100m 500mm x 100m 

※   UL certificated. UL file NO.MH15431
※2  T3500SBW: With both side release paper

Application Example
For adhesion at portions that need to be light resistance or black.
Top of page

Technical Data

1.Bonding strength at different temperatures(180° peeling) 180°Peeling strength test
Test Piece Condition
Substrate: Stainless steel plate (SUS304)
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Peel speed: 300mm/min  
Backing material: 25µm PET
Measuring condition: 23°C±5°C 60%±20%RH
  • [Left at RT for one hour and then at each temperature for 30 minutes before measurement ]
Results
2.Holding Power at different temperatures Holding power test
Test Piece Condition
Substrate: Stainless steel plate (SUS304)
Bonding area: 25mm x 25mm
Bonding condition: One stroke with 2-kg roller
Backing material: 25µm PET
  • [Left at RT for one hour and then at each temperature for 30 minutes before measurement ]
  • [Creep length after one-hour application of 1-kg load ]
Results
3.Reliability of bonding strength under different conditions
(180° peeling)		 180°Peeling strength test
Test Piece Condition
Substrate: Stainless steel plate (SUS304)
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Peel speed: 300mm/min  
Backing material: 25µm PET
  • [Left at RT for one hour and aged under each test condition before measurement ]
Results
4.Bonding strength on various type of substrate
(180° peeling)		 180°Peeling strength test
Test Piece Condition
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Measuring condition: 23°C±5°C 60%±20%RH
Peel speed: 300mm/min  
Backing material: 25µm PET
  • [Left at RT for one hour before measurement]
Results
5.Curved surface bending Curved surface bending test
Test Piece Condition
Substrate: ABS PLATE: 2.0 mm thickness 25mm x 200mm
Aluminum plate: 0.4 mm thickness 20mm x 150mm
Bonding condition: One stroke with 2-kg roller
Conditions for thermal shock test: Measure distance lifted after each cycle of "-40°C, 2 hr --> 80°C, 2 hr."
Results
Top of page
caution The technical data in this document, which was acquired based on reliable tests, does not guarantee full performance as per the documentation in any instance. Users assume total responsibility and risk for use of this product for any purpose under any usage conditions.