Strong adhesive type double coated tapes
Strong adhesive tape series with different-thickness nonwoven fabric carrier produced using non-solvent manufacturing method.
Products Category Double coated tapes
Please select the product name :
Comparison
UT1640BU

Product name

 UT1640BU

Suitable use

 For strong adhesion

Application

 Computers / AV / Cellular phones

Features
  • About twice the adhesion strength of our G-series tapes. Suitable for adhesion to glass or metal surfaces.
  • Good holding power even at elevated temperature.
  • Environmentally friendly non-solvent manufacturing method.
non-solvent manufacturing method
   

Structure

Specifications
Product name UT1640BU
Main component Acrylic base
Carrier Nonwoven fabric
Color Semi transparent
Adhesive thickness(µm) About 400
Release paper thickness(µm) About 130
Bonding strength(N/20mm) 31
St'd size (width & length) 480mm x 50m

Application Example
For adhesion of various types of metal and plastic.
Top of page

Technical Data
1.Bonding strength on various type of substrate (90° peeling) 90°Peeling strength test
Test Piece Condition
Tape width: 20mm
Bonding condition: One stroke with 2-kg roller
Measuring condition: 23°C±5°C 60%±20%RH
Peel speed: 300mm/min  
Backing material: 40µm Aluminum foil
  • [ Left at RT for one hour before measurement ]
Results
(N/20mm)
Substrate SUS Steel Aluminum Copper ABS PC Acrylic
90° peeling strength 30.9 32.1 17.4 28.5 16.1 13.2 19.6
2.Holding Power at different temperatures Holding power test
Test Piece Condition
Substrate: Stainless steel plate (SUS304)
Bonding area: 25mm x 25mm 
Bonding condition: One stroke with 2-kg roller
Backing material:  40µm Aluminum foil
  • [ Left at RT for one hour and then at each temperature for 30 minutes before measurement ]
  • [ Creep length after one hour application of 1-kg load ]
Results
Measurement temperature 80°C 120°C 150°C
Holding Power(mm) 1.2 1.5 2.1
Top of page
caution The technical data in this document, which was acquired based on reliable tests, does not guarantee full performance as per the documentation in any instance. Users assume total responsibility and risk for use of this product for any purpose under any usage conditions.